Nanocrystalline shear band

online order

  * Our company began to produce nanocrystalline and amorphous strips in 1995. It is the first private enterprise to produce nanocrystalline and amorphous strips in China.

* In 1998, our low loss nanocrystalline iron core was applied to the self-excited transformer of a fighter plane.
* Our transformer core was applied to national key projects such as Bird‘s Nest and the Three Gorges Project.
* Our automatic production line of nanocrystalline thin strip for wireless charging is independently designed and manufactured. Siemens automation technology is adopted and high-quality beryllium copper rollers are imported. In 2020, 11 patents were newly declared.
* The nanocrystalline strips produced for wireless charging has the advantages of high density, no pitting and high toughness. 
 

Physical characteristics

Material grade

Crystallization temperature

Curie temperature

Resistivity(μΩ.cm)

Saturation magnetic induction(T)

Saturation magnetostrictive coefficient

Density (g/cm³ )

1K107B

530

570

120

1.25

 0.000001

7.2

Standard magnetic properties

Material grade

Material composition

Relative initial permeability

(μ i)

Coercivity(A/m)

Saturation magnetic induction(T)

Iron loss(W/kg) 

P5/50K

Iron loss (W/kg) 

P1/100K

1K107B

FeCuNbSiB

50000~100000

1.5  

1.25

<85

<22

Strip specification

Width(mm)

Thickness (μm)

3.2/4/4.5/5/6/6.5/8/10/12/15/20/25/30

16/17/18/19/20/21/22/23/24